Proses adsorpsi logam oleh karbon aktif merupakan salah satu dari rangkaian unit proses yang diterapkan di industri pengolahan emas. Pada proses adsorpsi dilakukan pengadukan dengan mengalirkan udara dari dasar reaktor (aerasi) dan dibantu oleh agitator. Pengadukan bertujuan agar tidak terjadi pengendapan slurry serta karbon terdistribusi merata ke seluruh bagian reaktor, kontak antara slurry dengan karbon aktif intensif sehingga persentase adsorpsi tinggi. Penelitian ini bertujuan untuk mengetahui pengaruh variasi debit udara yang berperan sebagai pengaduk serta rasio massa karbon dengan volume slurry terhadap persentase adsorpsi logam Fe3+. Penelitian dilakukan pada skala laboratorium dengan berbagai pendekatan agar dapat merepresentasikan proses Carbon In Leach (CIL), yaitu menggunakan kolom adsorpsi dengan karakteristik mixed flow. Debit udara yang digunakan yakni 1 m3/h; 1,5 m3/h; dan 2 m3/h, sedangkan rasio massa karbon terhadap volume slurry yang digunakan yakni 15 g/L; 20 g/L; dan 25 g/L. Solid yang digunakan adalah tailing dari PT CSD (Cibaliung Sumberdaya) dengan ukuran partikel dari 63 μm hingga 125 μm. Konsentrasi besi yang digunakan merujuk pada konsentrasi besi yang terkandung pada slurry di PT CSD yaitu sebesar 400 hingga 500 ppm. Dari hasil penelitian didapatkan debit udara terbaik sebesar 2 m3/h dan rasio massa karbon dengan volume slurry terbaik sebesar 20 g/L dengan persen adsorpsi sebesar 53,3 %. Kata Kunci : Adsorpsi, CIL, Mixed Flow

The metal adsorption process by activated carbon is one of process unit series that applied in the gold processing industry. Stirring that occurs in the adsorption process is done by flowing the air from the bottom of reactor (aeration) and assisted by agitator. The slurry is stirred to prevent the solid to settle and to evenly distribute the activated carbon. The distribution of activated carbon is very important to enhance metal adsorption. This research aims to study the effect of air flow rate and the ratio of carbon mass to slurry on the adsorption process of Fe3+ metal. This research was conducted in a laboratory scale with various approaches in order to represent the Carbon In Leach (CIL), wich adsorption column is used with the characteristics of mixed flow. Air flow rate that used in this research were 1 m3/h; 1,5 m3/h; and 2 m3/h, and for the ratio of carbon mass to slurry volume were 15 g/L; 20 g/L; and 25 g/L. The tailing from PT CSD (Cibaliung Sumberdaya) was used for this research with particle size from 63 μm to 125 μm. The iron concentration that used in this research refers to the iron concentration of fresh slurry at PT CSD i.e. 400 to 500 ppm. The best air flow rate obtained from the result of this research was 2 m3/h, while the best ratio of carbon mass to slurry volume was 20 g/L resulted 53.3% adsorption. Key Words : Adsorption, CIL, Mixed Flow

http://digilib.polban.ac.id/gdl.php?mod=browse&op=read&id=jbptppolban-gdl-151411007f-10445